| 时效处理对Al0.5CoCrFeNi高熵合金微观组织结构和力学性能的影响 |
| |
| 引用本文： | 唐群华,赵亚光,蔡建宾,戴品强. 时效处理对Al0.5CoCrFeNi高熵合金微观组织结构和力学性能的影响[J]. 有色金属(冶炼部分), 2011, 0(4): 47-50. DOI: 10.3969/j.issn.1007-7545.2011.04.014 |
| |
| 作者姓名： | 唐群华 赵亚光 蔡建宾 戴品强 |
| |
| 作者单位： | 1. 福州大学材料科学与工程学院,福州,350108
2. 福州大学材料科学与工程学院,福州350108;福建工程学院材料科学与工程学院,福州350108 |
| |
| 基金项目： | 国家大学生创新性试验计划项目（091038629） |
| |
| 摘 要： | 对Al0.5CoCrFeNi高熵合金经不同温度时效处理24 h后的微观组织和力学性能进行研究。结果表明:时效处理前后,Al0.5CoCrFeNi高熵合金均由简单的体心立方相和面心立方相组成,组织主要为树枝晶形貌。但是,随着时效温度的升高(800℃和1 000℃),树枝晶析出弥散分布的针状第二相,且第二相数量不断增大。由于第二相的弥散强化作用,时效处理能显著提高合金的抗拉强度。
|
| 关 键 词： | 时效处理 微观组织 高熵合金 机械性能 |
| 收稿时间： | 2010-10-29 |
Effect of Aging Treatment on Microstructures and Mechanical Properties of Al0.5CoCrFeNi High-Entropy Alloy |
| |
| TANG Qun-hu,ZHAO Ya-guang,CAI Jian-bin and DAI Pin-qiang. Effect of Aging Treatment on Microstructures and Mechanical Properties of Al0.5CoCrFeNi High-Entropy Alloy[J]. Nonferrous Metals(Extractive Metallurgy), 2011, 0(4): 47-50. DOI: 10.3969/j.issn.1007-7545.2011.04.014 |
| |
| Authors: | TANG Qun-hu ZHAO Ya-guang CAI Jian-bin DAI Pin-qiang |
| |
| Affiliation: | TANG Qun-hua1,ZHAO Ya-guang1,CAI Jian-bin1,DAI Pin-qiang1,2(1.College of Materials Science and Engineering,Fuzhou University,Fuzhou 350108,China,2.Department of Materials Science and Engineering,College of Fujian Engineering,China) |
| |
| Abstract: | The microstructures and mechanical properties of Al0.5CoCrFeNi high-entropy alloy aged at temperatures range from 600 ℃ to 1 000 ℃ for 24 h were studied.The results show that FCC and BCC phase structures remain unchanged after aging treatment,and the microstructures mainly are dendrite.However,with the increase of aging temperature,dispersive second phase precipitates and the amount of second phase increases.Furthermore,the aging treatment can enhance tensile strength due to the dispersion strengthening of second phase. |
| |
| Keywords: | Aging treatment Microstructure High-entropy alloy Mechanical properties |