A Coprecipitation Coating Synthesis of SiC/YAG Composites |
| |
Authors: | Ning ZHANG Hongqiang RU Xudong SUN Qingkui CAI |
| |
Affiliation: | School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China;Materials Department, Shenyang University, Shenyang 110044, China |
| |
Abstract: | The α-SiC in 0.5 μm size powders were coated with Al2O3 and Y2O3 by a coprecipitation coating (CPC) method for fabrication of SiC/YAG composites. The same powder preparation was carried out by conventional mechanical mixing (MM) method for comparison. Two kinds of SiC/YAG composites were manufactured by pressureless sintering using the different powders, named CPC composite and MM composite thereafter respectively. It is shown that the CPC composite has the advantages of homogeneous distribution of YAG phase and of being sintered to high density at a low temperature, 100℃ lower than that of MM composite. The strength (573 Mpa) and hardness (23.3 Gpa) of the CPC composite are significantly higher than those (323 Mpa and 13.5 Gpa) of the MM composite, respectively. |
| |
Keywords: | Coprecipitation SiC/YAG composites Mechanical mixing method |
本文献已被 CNKI 万方数据 等数据库收录! |
| 点击此处可从《材料科学技术学报》浏览原始摘要信息 |
|
点击此处可从《材料科学技术学报》下载全文 |
|