| 钛调节阀的腐蚀分析和解决方案 |
| |
| 引用本文： | 翁小平. 钛调节阀的腐蚀分析和解决方案[J]. 燃料与化工, 2009, 40(4): 37-39 |
| |
| 作者姓名： | 翁小平 |
| |
| 作者单位： | 宝钢化工有限公司,上海,200942 |
| |
| 摘 要： | 介绍了钛调节阀的损坏和腐蚀情况,分析了阀芯的断裂原因。分析表明,溶液中含氟离子和冲刷腐蚀是调节阀损坏的原因,通过改进阀门的结构和对阀芯、阀座进行表面处理可以延长调节阀的寿命。
|
| 关 键 词： | 钛调节阀 腐蚀 损坏 |
Corrosion analysis and solution for titanium regulating valve |
| |
| Weng Xiaoping. Corrosion analysis and solution for titanium regulating valve[J]. Fuel & Chemical Processes, 2009, 40(4): 37-39 |
| |
| Authors: | Weng Xiaoping |
| |
| Affiliation: | Chemical Industrial Co.;Ltd;of Baosteel;Shanghai 200942;China |
| |
| Abstract: | The damage and corrosion of titanium regulating valve is described and the fracture cause of valve core is analyzed.The analysis shows that the fluorine containing ion in solution and flushing are the major causes of the damage of regulating valve.The service life of the regulating valve can be prolonged by the improvement of the valve structure and surface treatment of valve core and valve seat. |
| |
| Keywords: | Titanium regulating valve Corrosion Damage |