Optical temperature sensor based on upconversion luminescence of Er3+ doped GdTaO4 phosphors

For the development of optical temperature sensor, a series of GdTaO₄ phosphors with various Er³⁺-doping concentrations (0, 1, 5, 10, 25, 35, 50 mol%) were synthesized by a solid-state reaction method. The monoclinic crystalline structure of the prepared samples was determined by X-ray diffraction (XRD). Under excitations of 980 and 1550 nm lasers, the multi-photon-excited green and red upconversion (UC) luminescence emissions of Er³⁺ were studied, and the critical quenching concentration of Er³⁺-doped GdTaO₄ phosphor was derived to be 25 mol%. By changing the pump power of laser, it was found that the two-photon and three-photon population processes happened for the UC emissions of Er³⁺-doped GdTaO₄ phosphors excited by 980 and 1550 nm lasers, respectively. Furthermore, based on the change of thermo-responsive green UC luminescence intensity corresponding to the ²H_11/2 → ⁴I_15/2 and ⁴S_3/2 → ⁴I_15/2 transitions of Er³⁺ with temperature, the optical temperature sensing properties of Er³⁺-doped GdTaO₄ phosphor were investigated under excitations of 980 and 1550 nm lasers by using the fluorescence intensity ratio (FIR) technique. It was obtained that the maximum absolute sensitivity (S_A) and relative sensitivity (S_R) of Er³⁺-doped GdTaO₄ phosphors are as high as 0.0041 K^?1 at 475 K and 0.0112 K^?1 at 293 K, respectively. These significant results suggest that the Er³⁺-doped GdTaO₄ phosphors are a promising candidate for optical temperature sensor.