Fabrication of high-efficiency anatase TiO2 photocatalysts using electrospinning with ultra-violet treatment

In metal oxide nanofiber fabrication using the electrospinning method, heat treatment is performed at temperatures of 500°C or higher for crystallization and polymer desorption. Therefore, it is difficult to fabricate low-temperature phase metal oxides that crystallize at low temperatures. TiO₂, a representative metal oxide often used as photocatalysts, is known to have higher photocatalytic activity in the low-temperature phase (anatase structure) than in the high-temperature phase (rutile structure). Studies on the fabrication of TiO₂ anatase nanofibers using conventional electrospinning have reported disadvantages such as the partial expression of rutile structures and low crystallinity. This study developed an anatase TiO₂ nanofiber as a high-efficiency catalyst based on the electrospinning method and a residual organic matter cleaning method that employs ultra-violet (UV) light. We fabricated nanofibers using the electrospinning method and implemented TiO₂ nanofibers with the anatase structure through heat treatment at 260°C. Residual organics remaining after heat treatment of the fabricated crystalized TiO₂ nanofibers were removed by exposing them to UV light, thereby improving photocatalytic efficiency. The photocatalytic efficiency of the fabricated TiO₂ nanofibers was confirmed through a methylene blue (MB) decomposition experiment under visible light irradiation. The photocatalytic efficiency (time taken for the concentration of the MB solution to reach 50%) of the UV-treated TiO₂ nanofibers was approximately six times higher than of P25 and the heat-treated nanofibers.