| 钴掺杂锰氧化物水系锌离子电池正极材料的制备与电化学性能 |
| |
| 引用本文： | 胡入丹,孙敬文,刘一凡,钱惺悦,张丽童,朱俊武. 钴掺杂锰氧化物水系锌离子电池正极材料的制备与电化学性能[J]. 机械工程材料, 2021, 45(1): 20-27. DOI: 10.11973/jxgccl202101004 |
| |
| 作者姓名： | 胡入丹 孙敬文 刘一凡 钱惺悦 张丽童 朱俊武 |
| |
| 作者单位： | 南京理工大学,软化学与功能材料教育部重点实验室,先进微纳米材料及装备协同创新中心,南京 210094;南京理工大学,软化学与功能材料教育部重点实验室,先进微纳米材料及装备协同创新中心,南京 210094;南京理工大学,软化学与功能材料教育部重点实验室,先进微纳米材料及装备协同创新中心,南京 210094;南京理工大学,软化学与功能材料教育部重点实验室,先进微纳米材料及装备协同创新中心,南京 210094;南京理工大学,软化学与功能材料教育部重点实验室,先进微纳米材料及装备协同创新中心,南京 210094;南京理工大学,软化学与功能材料教育部重点实验室,先进微纳米材料及装备协同创新中心,南京 210094 |
| |
| 基金项目： | 江苏省自然科学基金资助项目;国家自然科学基金资助项目;中央高校基本科研专项资金资助项目 |
| |
| 摘 要： | 以硝酸锰和硝酸钴为原料,通过溶剂热反应、水解和煅烧制备了可作为水系锌离子电池正极材料的钴掺杂锰氧化物,研究了钴掺杂锰氧化物的微观结构及电化学性能.结果表明:所制备的钴掺杂锰氧化物h-CoMn3.2Ox具有分级核壳结构,多孔壳表面存在径向尺寸大于100 nm的花瓣状纳米片,壳和纳米片均由平均粒径为5 nm的一次粒子构成,...
|
| 关 键 词： | 锰氧化物 钴掺杂 分级结构 水系锌离子电池 电化学性能 |
Preparation and Electrochemical Performance of Cobalt-Doped Manganese Oxide Aqueous Zinc-ion Battery Cathode Material |
| |
| HU Rudan,SUN Jingwen,LIU Yifan,QIAN Xingyue,ZHANG Litong,ZHU Junwu. Preparation and Electrochemical Performance of Cobalt-Doped Manganese Oxide Aqueous Zinc-ion Battery Cathode Material[J]. Materials For Mechanical Engineering, 2021, 45(1): 20-27. DOI: 10.11973/jxgccl202101004 |
| |
| Authors: | HU Rudan SUN Jingwen LIU Yifan QIAN Xingyue ZHANG Litong ZHU Junwu |
| |
| Affiliation: | (Key Laboratory for Soft Chemistry and Functional Materials,Ministry of Education,Collaborative Innovation Center for Advanced Micro and Nano Materials and Equipment,Nanjing University of Science and Technology,Nanjing 210094,China) |
| |
| Abstract: | The cobalt-doped manganese oxide for aqueous zinc-ion battery cathode material was prepared by solvothermal,hydrolyzing and annealing with cobalt nitrate and manganese nitrate as raw materials.The microstructure and electrochemical performance of cobalt-doped manganese oxide was investigated.The results show that the prepared cobalt-doped manganese oxide h-CoMn3.2Ox had a hierarchical yolk-shell structure,and the porous shell surface was decorated with petal-like nanosheets with radial dimension of more than 100 nm.Both of the shell and nanosheets were composed of primary nanoparticles with average size of 5 nm.Cobalt-doping endowed manganese oxides with small size and delicate structure.h-CoMn3.2Ox had the manganosite MnO crystal structure.Compared with monometallic manganese oxide,h-CoMn3.2Ox exhibited relatively large specific surface areas and specific capacities,and had good cyclic stability.The energy-storage behavior of h-CoMn3.2Ox was attributed to sequent co-insertion of H+and Zn2+. |
| |
| Keywords: | manganese oxide cobalt-doping hierarchical structure aqueous zinc-ion battery electrochemical performance |