| 服役时间对1Cr5Mo钢制高温紧固螺母显微组织和力学性能的影响 |
| |
| 引用本文： | 张腾雨,韩涛,吴术全,江峰,张志博,姜世凯. 服役时间对1Cr5Mo钢制高温紧固螺母显微组织和力学性能的影响[J]. 机械工程材料, 2021, 45(2): 61-65. DOI: 10.11973/jxgccl202102011 |
| |
| 作者姓名： | 张腾雨 韩涛 吴术全 江峰 张志博 姜世凯 |
| |
| 作者单位： | 西安交通大学金属材料强度国家重点实验室,西安 710049;西安交通大学金属材料强度国家重点实验室,西安 710049;西安交通大学金属材料强度国家重点实验室,西安 710049;西安交通大学金属材料强度国家重点实验室,西安 710049;西安热工研究院有限公司,西安 710054;华能沁北发电有限责任公司,济源 459012 |
| |
| 摘 要： | 针对某火电厂超临界机组汽轮机1Cr5Mo钢制紧固螺母服役后硬度大幅下降现象,在566℃下对1Cr5Mo钢制螺母进行时效试验(等效于服役),研究了时效时间对显微组织和力学性能的影响,并与566℃下服役约105 h螺母的组织和性能进行了对比.结果表明:在不高于566℃的条件下,1Cr5Mo钢制螺母显微组织转变缓慢,时效28...
|
| 关 键 词： | 高温螺母 1Cr5Mo钢 碳化物 马氏体 固溶强化 |
Effect of Service Time on Microstructure and Mechanical Properties of High Temperature 1Cr5Mo Steel Fastening Nut |
| |
| ZHANG Tengyu,HAN Tao,WU Shuquan,JIANG Feng,ZHANG Zhibo,JIANG Shikai. Effect of Service Time on Microstructure and Mechanical Properties of High Temperature 1Cr5Mo Steel Fastening Nut[J]. Materials For Mechanical Engineering, 2021, 45(2): 61-65. DOI: 10.11973/jxgccl202102011 |
| |
| Authors: | ZHANG Tengyu HAN Tao WU Shuquan JIANG Feng ZHANG Zhibo JIANG Shikai |
| |
| Affiliation: | (State Key Laboratory for Mechanical Behavior of Materials,Xi′an Jiaotong University,Xi'an 710049,China;Xi′an Thermal Power Research Institute Co.,Ltd.,Xi'an 710054,China;Huaneng Qinbei Power Generation Co.,Ltd.,Jiyun 159012,China) |
| |
| Abstract: | The hardness of the lCr5 Mo steel fastening nut of a supercritical unit steam turbine in a thermal power plant was reduced significantly after service.Aiming at this phenomenon,the aging tests(equivalent to service)of the 1 Cr5 Mo steel nut were carried out at 566℃.The effect of aging time on the microstructure and mechanical properties was studied,and the microstructure and performance were compared with those of the nut served at 566℃for 10~5 h.The results show that at temperatures not higher than 566℃,the microstructure of the 1 Cr5 Mo steel nut changed slowly;the microstructure was still martensite and carbide after aging for 2880 h.But the microstructure changed to tempered sorbite after service for 10~5 h.With the extension of the aging/service time,the carbides migrated and concentrated from the inside grain to the grain boundary,and became obviously coarsened.The deterioration of the structure led to the reduction of the hardness,strength,and impact energy of the nut. |
| |
| Keywords: | high temperature nut 1Cr5Mo steel carbide martensite solution strengthening |