Zwillingsbildung bei der thermischen Ermüdung der Mg‐Basislegierung AZ31 |
| |
Authors: | B Scholtes Prof Dr‐Ing habil M Krauß |
| |
Affiliation: | Institut für Werkstofftechnik – Metallische Werkstoffe, Universit?t Kassel, Sophie‐Henschel‐Haus, M?nchebergstr. 3, 34125 Kassel, Fax: 0561 804 3662 |
| |
Abstract: | Twinning at thermal fatigue of magnesium alloy AZ31 In this paper results of thermal fatigue tests of the magnesium base alloy AZ31 carried out in a temperature range between ‐50 °C and +290 °C are presented. Specimens were loaded under constant total strain and uniaxial homogeneous stresses. The resulting materials behaviour is described by stress amplitudes, plastic strain amplitudes and mean stresses as a function of the number of thermal loading cycles. It is well known that AZ31 shows different stress‐strain behaviour during tensile and compressive loading resp. at lower temperatures due to the fact that mechanical twinning depends on the loading direction. However untwinning processes may occur during unloading and reloading in the opposite direction. As a consequence, during the first thermal loading cycles, typical consequences of the formation and the dissolution of twins are observed. The interaction of deformation, recovery and recrystallization processes, characteristic for individual temperature ranges are discussed in detail to analyze the damage progress during thermal fatigue. |
| |
Keywords: | Thermische Ermü dung Magnesium Zwillingsbildung AZ31 Thermal fatigue magnesium twinning AZ31 |
|
|