| 钒钛磁铁矿冷压含碳球团强度性能研究 |
| |
| 引用本文： | 曹明明,张建良,王春龙,邢相栋,薛逊.钒钛磁铁矿冷压含碳球团强度性能研究[J].烧结球团,2012,37(1):35-38. |
| |
| 作者姓名： | 曹明明 张建良 王春龙 邢相栋 薛逊 |
| |
| 作者单位： | 1. 北京科技大学冶金与生态工程学院,北京,100083
2. 攀枝花钢铁研究院,四川攀枝花,617000 |
| |
| 基金项目： | “十一五”国家科技支撑计划重大项目(2008BAB32B05) |
| |
| 摘 要： | 基于转底炉直接还原工艺,以钒钛磁铁矿为原料进行压制球团工艺研究,以湿球落下强度作为考察指标,通过正交实验研究了矿粉粒度、煤粉粒度、配碳量及水分等因素对该指标的影响,并对其影响规律进行了分析。得出最佳压球工艺参数为:矿粉和煤粉中-200目比例分别占15%和65%,配碳量(C/O)为1.2,水分加入量为11%。此组合下的湿球落下强度为14.8次,完全可以满足转底炉生产要求。
|
| 关 键 词： | 钒钛磁铁矿 含碳球团 落下强度 压球 |
Research on Strength Performance of Cold-briquetted Carbon-containing Pellet of Vanadium Titano-magnetite |
| |
| CAO Ming-ming
,
ZHANG Jian-liang
,
WANG Chun-long
,
XING Xiang-dong
,
XUE Xun.Research on Strength Performance of Cold-briquetted Carbon-containing Pellet of Vanadium Titano-magnetite[J].Sintering and Pelletizing,2012,37(1):35-38. |
| |
| Authors: | CAO Ming-ming ZHANG Jian-liang WANG Chun-long XING Xiang-dong XUE Xun |
| |
| Affiliation: | 1.School of Metallurgical and Ecological Engineering,Beijing University of Science and Technology,Beijing 100083;2.Panzhihua Iron&Steel Research Institute,Panzhihua 617000,Sichuan) |
| |
| Abstract: | Based on the rotary hearth furnace(RHF) direct reduction process,vanadium titano-magnetites are used as raw materials for research of cold briquetting pelletizing process.The influences of ore fines particle size,coal fines particles size and carbon ratio etc,on the wet green drop index were studied through orthogonal experiment,and their influencing regularities were analyzed.The optimal process parameters are as follows:the ore fines and coal fines should contain minus 200 mesh 15% and 65% respectively,C/O(carbon ratio) is 1.2 and moisture water addition is 11%.Under this condition,the wet-drop strength can be up to 14.9 times,which fully meets the requirement of the rotary hearth furnace (RHF) production process. |
| |
| Keywords: | vanadium titano-magnetite carbon-containg pellet drop strength briquetted pellet |