Characterization of W80Cu20 alloy sheet prepared by hot-rolling
Authors:Hu-Ping Guo  Wen-Ge Chen  Hui Zhang
Affiliation:1. School of Materials Science and Engineering, Xi’an University of Technology, Xi’an, 710048, China
Abstract:Multi-pass hot-rolling technique was used to fabricate W80Cu20 alloy, and its properties were characterized in this paper. Results show that the W-Cu alloy sheets with a thickness of 0.5 mm and a relative density of 99.87 % can be successfully made using this new technique at 800 °C. In hot-rolling process, Cu phases are closely surrounded by W particles under the rolling stress to form a network microstructure, thus making significant increase in electrical and thermal conductivity up to 53.00 % and 24.44 %, respectively. Transverse and longitudinal hardness of the W–Cu sheets significantly increase due to the enhanced densification and deformation strength. Similar to that of the raw materials, three fracture types were observed in the hot-rolled materials, i.e., ductile fracture of Cu binding phases, trans-granular fracture of W phases, and W–W interfacial fracture.
Keywords:
本文献已被 维普 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号