Low-temperature firing and microwave dielectric properties of 16CaO–9Li2O–12Sm2O3–63TiO2 ceramics with V2O5 addition

The sintering behaviors and microwave dielectric properties of the 16CaO–9Li₂O–12Sm₂O₃–63TiO₂ (abbreviated CLST) ceramics with different amounts of V₂O₅ addition had been investigated in this paper. The sintering temperature of the CLST ceramic had been efficiently decreased by nearly 100 °C. No secondary phase was observed in the CLST ceramics and complete solid solution of the complex perovskite phase was confirmed. The CLST ceramics with small amounts of V₂O₅ addition could be well sintered at 1200 °C for 3 h without much degradation in the microwave dielectric properties. Especially, the 0.75 wt.% V₂O₅-doped ceramics sintered at 1200 °C for 3 h have optimum microwave dielectric properties of Kr = 100.4, Q × f = 5600 GHz, and TCF = 7 ppm/°C. Obviously, V₂O₅ could be a suitable sintering aid that improves densification and microwave dielectric properties of the CLST ceramics.