Abstract: | Previously it was found that casting could be carried out efficiently without strain formation by radiation-induced polymerization of glass-forming monomers. Two types of strain were observed in casting: thermal stream type, which was studied previously, and remained stress type. In this report, the effect of various factors on the formation of remaining stress-type strain in radiation-induced casting polymerization was studied. It was found that the molecular weight of prepolymer did not affect strain formation, while prepolymer concentration and viscosity of the system had a serious influence on strain formation. It could be deduced that this type of strain formed as a result of remaining inner stress due to poor relaxation of the shrinking stress. It was realized that less volume shrinkage of glass-forming monomers accompanying casting polymerization reduced the strain formation of this type in radiation-induced casting polymerization at low temperatures. |