Stresses and Microstructural Development of Thermal Barrier Coatings Using AIP/D-gun Two-Step Processing

After depositing a Ni–32Co–20Cr–8Al–0.5Y–1Si–0.03B (wt%) bond coat on a Ni-base superalloy using arc ion plating (AIP), a ceramic top coat with hollow spherical powder of ZrO₂–8 wt%Y₂O₃ (HSP–YSZ) was deposited using detonation gun (D-gun) spraying. Thermal exposure behaviors of thermal barrier coatings (TBCs) were investigated at 1100°C. The thermal growth oxides (TGO) layer thickened and became more undulated during thermal exposure. Yttrium aluminum garnet (YAG) was observed within TGO, which produced thickness imperfections and thus aided to build up out-of-plane stresses. As a result, radial cracks initiated at the defects around TGO imperfections and separation developed through crack nucleation, propagation, and coalescence at the weaker TGO/bond coat interface. With further thermal exposure, coalescence of interfacial separations created a connected crack. The TBC detached and final failure occurred at the TGO/bond coat interface, leading to spallation of TBC when cooling to ambient. The stress distributions in the TGO layer with different thermal exposure times were also measured using luminescence spectroscopy. The stresses were independent of time after a transient period from θ-Al₂O₃ to α-Al₂O₃ scale. It is suggested that the lifetime of AIP/D-gun TBCs with an HSP–YSZ coat is controlled by the initiation and linking of a sub-critical interfacial crack.