Magnetic properties of (Fe)1−x–(Al2O3)x and (Fe50Ni50)1−x–(Al2O3)x nanocomposite magnetic media synthesized using gel like Al2O3 matrix

Composites with ferromagnetic nanoparticles, Fe and Fe₅₀Ni₅₀, dispersed in Al₂O₃ have been synthesized by a solution phase technique. The structure and magnetic properties of these composites with varying fractions of Al₂O₃ have been investigated. Both Fe and Fe₅₀Ni₅₀ nanoparticles are amorphous in the as-prepared state and become crystalline on heat treating with near equilibrium lattice parameters of 0.287 nm and 0.358 nm respectively. The interparticle distance increases with increasing Al₂O₃ from 0 wt.% to 20 wt.%. The size of Fe nanoparticles is 40 nm while the Fe₅₀Ni₅₀ nanoparticles are 20 nm in size. The Fe and Fe₅₀Ni₅₀ nanoparticles dispersed composites are found to be ferromagnetic at room temperature both in the as-prepared and heat treated conditions with clear coercive fields of 5.5–35 × 10³ A m⁻¹. The saturation magnetization increases by orders of magnitude on heat treatment, for e.g. from <1.0 emu g⁻¹ to 143.4 emu g⁻¹ for Fe–15 wt.% Al₂O₃ and 95.6 emu g⁻¹ for Fe₅₀Ni₅₀–15 wt.% Al₂O₃. The Fe-composites exhibit a Curie transition at 1000 K while the Fe₅₀Ni₅₀ composites exhibit a transition at 880 K, both temperatures close to bulk values.