A study of microstructure and performance of cast Fe–8Cr–2B alloy |
| |
Authors: | M Yue F Han‐guang M Shang‐lin L Yong‐ping |
| |
Affiliation: | 1. School of Materials Science and Engineering, Beijing University of Technology, , Beijing, 100124 P.R. China;2. Shenyang Research Institute of Foundry, , Shenyang, 110022 Liaoning province, P.R. China |
| |
Abstract: | The effects of quenching temperature on microstructure and hardness of cast Fe–8Cr–2B alloy containing 0.3 wt% C, 2.0 wt% B, 8.0 wt% Cr, 0.6 wt% Si, and 0.8 wt% Mn were investigated by optical microscopy (OM), scanning electron microscopy (SEM), X‐ray diffraction (XRD), Rockwell hardness and Vickers microhardness testers. The experimental results indicate that the as‐cast microstructure of cast Fe–8Cr–2B alloy consists of M2B (M = Fe, Cr), M7(C, B)3, α‐Fe, and γ‐Fe. The dendritic matrix composed of lath martensite mixed with a small amount of retained austenite, and the netlike boride M2B distribute in the grain boundary. After quenching between 950 °C and 1100 °C, the netlike eutectic boride are broken up and a new phase‐M23(C, B)6 which is distributed in the shape of sphere or short rod‐like are precipitated from the matrix. Both the macrohardness and microhardness of specimens increase with the increasing quenching temperature. At about 1050 °C, the hardness reaches the maximum value. However, when the temperature exceeds 1050 °C, the hardness will decrease slightly. With the increase of tempering temperature, the hardness of cast Fe–8Cr–2B alloy quenching from 1050 °C decreases gradually and its impact toughness increases slightly. Crusher hammer made of cast Fe–8Cr–2B alloy quenching from 1050 °C and tempering from 300 °C has good application effect, and its service life improves by 150–180% than that of high manganese steel hammer. |
| |
Keywords: | Gusslegierung Fe8Cr2B Anlasstemperatur Boride Gefü ge Mechanisch‐technologische Eigenschaften Hammerbrecher Cast Fe– 8Cr– 2B alloy quenching temperature boride microstructure mechanical performance crusher hammer |
|
|