Thermodynamics of oxygen solutions in Fe-Ni-V melts

The oxygen solutions in Fe-Ni melts with up to 5% V are analyzed thermodynamically. The results of the works in which the fields of the vanadium-deoxidized oxide phases in iron and nickel were determined are generalized. The thermodynamic model developed for the calculation of the deoxidation of iron-nickel alloys with vanadium is shown to be adequate. The deoxidizing capacity of vanadium decreases insignificantly as the nickel content in the melt increases to 20% and increases substantially as the nickel content increases further. The oxygen solubility curves pass through a minimum, whose position changes from 2.3192% V for pure iron to 0.7669% V for pure nickel. We determined the equilibrium point V]* between the (Fe, Ni)V₂O₄ and V₂O₃ oxide phases for alloys of six compositions at 1873 K. In nickel, V]* is almost 200 times lower than in iron. The deoxidation of the Fe-40% Ni melt with vanadium is studied experimentally, and the experimental results agree satisfactorily with the calculated data.