Microstructural evolution of a PM TiAl alloy during heat treatment in α+γ phase field |
| |
作者姓名: | SU Meike ZHENG Lijing LANG Zebao YAN Jie ZHANG Hu |
| |
作者单位: | [School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100191, China [1] Aerospace Research Institute of Materials & Processing Technology, Beijing 100076, China [2], Beijing 100076, China |
| |
基金项目: | supported by the National Natural Science Foundation of China (No. 51101003) |
| |
摘 要: | In this study,the effect of temperatures and cooling rates of heat treatment on the microstructure of a powder metallurgy (PM) Ti-46Al-2Cr-2Nb-(B,W) (at.%) alloy was studied.Depending on the cooling rate and temperature,the different structures were obtained from the initial near-γ (NG) microstructures by heat treatment in the α+γ field.The results show that the microstructures of samples after furnace cooling (FC) consist primarily of equiaxed γ and α2 grains,with a few grains containing lamellae.Duplex microstructures consist mainly of γ grains and lamellar colonies were obtained in the quenching into another furnace at 900℃ (QFC) samples.However,further increasing of the cooling rate to air cooling (AC) induces the transformation of α→α2 and results in a microstructure with equiaxed γ and α2 grains,and no lamellar colonies are found.
|
关 键 词: | γ-TiAl-based alloys powder metallurgy heat treatment duplex structure phase volume fractions |
本文献已被 CNKI 维普 万方数据 SpringerLink 等数据库收录! |
|