Sol—Gel Fabrication of Pb(Zr0.52 Ti0.48)O3 Thin Films Using Lead Acetylacetonate as the Lead Source
Authors:Ulagaraj Selvaraj  Keith Brooks  Alamanda V. Prasadarao  Sridhar Komarneni  Rustum Roy  L. Eric Cross
Affiliation:Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
Abstract:Lead zirconium titanate (PZT) thin films of the morphotropic phase boundary composition [Pb(Zr0.52Ti0.43)O3] were deposited on platinum-coated silicon by a modified sol-gel process using lead acetylacetonate as the lead source. The precursor solution for spin coating was prepared from lead acetylacetonate, zirconium n -butoxide, and titanium isopropoxide. The use of lead acetylacetonate instead of the widely used lead acetate trihydrate provided more stability to the PZT precursor solution. Films annealed at 700°C for 12 min formed well-crystallized perovskite phase of Pb(Zr0.52Ti0.48)O3. Microstructures of these films indicated the presence of submicrometer grains (0.1 to 0.2 μm). The dielectric constant and loss values of these films measured at 10 kHz were approximately 1200 and 0.04, respectively, while the remanent polarization and coercive field were ∼ 13 μC/cm2 and ∼ 35 kV/cm. Aging of the solution had almost no effect on the dielectric and ferroelectric properties of these films.
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号