The Effects of Sodium Chloride Solution on Fretting Wear Behavior of Nickel Based Alloy in Partial Slip Regime |
| |
Authors: | Jie Li Xiaohui Tu Wei Li |
| |
Affiliation: | 1. Institute of Advanced Wear &2. Corrosion Resistant and Functional Materials, Jinan University, Guangzhou 510632, P. R. China |
| |
Abstract: | The investigations on fretting wear behaviors of nickel based alloy in NaCl solution and atmosphere indicated that wear mechanism and regional transformation from partial slip regime (PSR) to the mixed regime (MR) are significantly affected by NaCl solution. The crevice corrosion induced by synergy of chloride ion and deformed asperities caused wear mechanism changed from adhesive and oxidation wear (PSR in atmosphere) to abrasive and oxidation wear (PSR in NaCl solution) and to oxidation and delamination wear (MR in NaCl solution), meanwhile accelerated the regional transformation from PSR to MR. However, the annular fatigue crack was almost unaffected by NaCl solution, which propagated along the direction of 40-50° to surface in the mode of transgranular and intergranular in all conditions. |
| |
Keywords: | Fretting wear Nickel based alloy Crack Oxidation |
|
|