| Microstructure and properties of aging Cu–Cr–Zr alloy |
| |
| 作者姓名： | Kun Wang Ke-Fu Liu Jing-Bo Zhang |
| |
| 作者单位： | [1]Institute of Electric Lighting Source, Fudan University,Shanghai 200433, China [2]No. 23 Research Institute, China Electronics Technology GroupCorporation, Shanghai 201900, China |
| |
| 基金项目： | This work was financially supported by the Special Foundation for Technology Research and Development in Research Institute of China （No. 2011DIA5k023）. |
| |
| 摘 要： | The crystallography and morphology of precipitate particles in a Cu matrix were studied using an aged Cu–Cr–Zr alloy by transmission electron microscopy(TEM) and high-resolution transmission electron microscopy(HRTEM). The tensile strength and electrical conductivity of this alloy after various aging processes were tested. The results show that two kinds of crystallographic structure associated with chromium-rich phases, fcc and bcc structure, exist in the peak-aging of the alloy. The orientation relationship between bcc Cr precipitate and the matrix exhibits Nishiyama–Wasserman orientation relationship. Two kinds of Zr-rich phases(Cu4Zr and Cu5Zr)can be identified and the habit plane is parallel to {111}Cu plane during the aging. The increase in strength is ascribed to the precipitation of Cr- and Zr-rich phase.
|
| 关 键 词： | Cu–Cr–Zr alloy Aging process Crystallography Morphology Strengthening mechanism |
| 本文献已被 CNKI 维普 SpringerLink 等数据库收录！ |