Coercivity variation in exchange-coupled Fe/FePt bilayer with perpendicular magnetization

The soft/hard Fe/FePt film with perpendicular magnetization has been deposited on a glass substrate. The (001) oriented L1₀ FePt film was obtained when annealed by rapid thermal process at 800 °C and a Fe layer was deposited at room temperature with thicknesses of 2 nm to 20 nm. Controlling the Fe layer thickness allowed modification of the hysteresis loops from out-of-plane rigid magnet to in-plane exchange-spring like magnet due to the nanometer scale interface coupling. When the Fe layer thickness increased to 2 nm, the out-of-plane coercivity is reduced to 5.9 kOe but the remanence ratio (0.98) is still high. The Fe (2 nm)/FePt film shows perpendicular magnetization with linear in-plane hysteresis loop. The remanence ratio is reduced to 0.85 when the Fe layer thickness increased to 5 nm. When the Fe layer thickness was varied up to 10-20 nm, the in-plane hysteresis loop shows exchange-spring like behavior with two-step magnetization reversal processes. The films with perpendicular coercivity were moderated by the thickness of soft magnetic layer.