电解复合磁力研磨GH4169管内表面的光整研究
引用本文:谭悦,陈燕.电解复合磁力研磨GH4169管内表面的光整研究[J].电镀与精饰,2020(1):27-32.
作者姓名:谭悦  陈燕
作者单位:贵州航天天马机电科技有限公司;辽宁科技大学机械工程与自动化学院
基金项目:国家自然科学基金项目(51775258)。
摘    要:为解决GH4169合金管内表面质量问题,降低其表面粗糙度,本文采用电解复合磁力研磨光整加工方法进行了试验,研究了在电解复合磁力研磨条件下,磁粒粒径、电解液温度、电解电压对管内壁表面质量的影响,寻求了最优的工艺参数组合。结果表明,在磁粒粒径为185μm,电解液温度为35℃,电解电压为9 V的条件下,采用电解复合磁力研磨法对GH4169合金管内表面加工25 min,管内表面粗糙度Ra可由原始的1.8μm降至0.11μm。表面缺陷得到有效去除,表面质量得到了明显的改善。管内表面残余应力由+92 MPa转变为-68 MPa,获得了更好的应力状态,提高了表面抗疲劳强度。

关 键 词:镍基合金  电解复合磁力研磨  表面粗糙度  残余应力  钝化

Surface Finishing of GH4169 Tube by Electrolytic Composite Magnetic Grinding
TAN Yue,CHEN Yan.Surface Finishing of GH4169 Tube by Electrolytic Composite Magnetic Grinding[J].Plating & Finishing,2020(1):27-32.
Authors:TAN Yue  CHEN Yan
Affiliation:(Guizhou Aerospace Tianma Mechanical and Electrical Technology Co.Ltd.,Zunyi 563000,China;School of Mechanical Engineering and Automation,University of Science and Technology Liaoning,Anshan 114051,China)
Abstract:In this paper,in order to improve the surface quality and reduce the surface roughness of GH4169 alloy tube,the electrolytic composite magnetic abrasive finishing method was carried out in the experiment.The effects of magnetic particle size,electrolyte temperature and electrolyte voltage on the inner surface quality of tube under electrolytic composite magnetic abrasion were studied and the optimum combination of process parameters was sought.The results show that the surface roughness of GH4169 alloy tube is reduced from 1.8μm to 0.11μm after electrolytic composite magnetic grinding for25 min under the following conditions:magnetic particle size of 185μm,electrolyte temperature of35℃and electrolytic voltage of 9 V.The surface defects were effectively removed and the surface quality was obviously improved.The residual stress on the inner surface of the tube is changed from+92 MPa to-68 MPa,a better stress state is obtained and the surface fatigue strength is increased.
Keywords:nickel-based alloy  electrolytic composite magnetic grinding  surface roughness  residual stress  passivation