The corrosion behavior of Fe-Nb-Al alloys in H2/H2O/H2S atmospheres

The corrosion behavior of eight Fe-Nb-Al ternary alloys was studied over the temperature range 700–980°C in H₂/H₂O/H₂S atmospheres. The corrosion kinetics followed the parabolic rate law for all alloys at all temperatures. The corrosion rates were reduced with increasing Nb content for Fe-x Nb -3Al alloys, the most pronounced reduction occurred as the Nb content increased from 30 to 40 wt.%. The corrosion rate of Fe-30Nb decreased by six orders of magnitude at 700°C and by five orders of magnitude at 800°C or above by the addition of 10 wt.% aluminum. The scales formed on low-Al alloys (3 wt.% Al) were duplex, consisting of an outer layer of iron sulfide (with Al dissolved near the outer-/inner-layer interface) and an inner complex layer of Fe_xNb₂S₄(FeNb₂S₄ or FeNb₃S₆), FeS, Nb₃S₄ (only detected for Nb contents of 30 wt.% or higher) and uncorroded Fe₂Nb. No oxides were detected on the low-Al alloys after corrosion at any temperature. Platinum markers were found to be located at the interface between the inner and outer scales for the low-Al alloys, suggesting that the outer scale grew by the outward transport of cations (Fe and Al) and the inner scale grew by the inward transport of sulfur. The scales formed on high-Al alloys (5 wt.% Al) were complex, consisting primarily of Nb₃S₄, Al₂O₃ and (Fe, Al)_xNb₂S₄, and minor amounts of (Fe, Al)S and uncorroded intermetallics (FeAl and Fe₂Nb). The formation of Nb₃S₄ and Al₂O₃ blocked the transport of iron through the inner scale, resulting in the significant reduction of the corrosion rates.