| Abstract: | Poly(urethane‐benzoxazine)/clay hybrid nanocomposites (PU/Pa–OMMTs) were prepared from an in situ copolymerization of a polyurethane (PU) prepolymer and a monofunctional benzoxazine monomer, 3‐phenyl‐3,4‐dihydro‐2H‐1,3‐benzoxazine (Pa), in the presence of an organophilic montmorillonite (OMMT), by solvent method using DMAc. OMMT was made from cation‐exchange of Na‐montmorillonite (MMT) with dodecyl ammonium chloride. The formation of the exfoliated nanocomposite structures of PU/Pa‐OMMT was confirmed by XRD from the disappearance of the peak due to the basal diffraction of the layer‐structured clay found in both MMT and OMMT. DSC showed that, in the presence of OMMT, the curing temperature of PU/Pa lowered by ca. 60°C for the onset and ca. 20°C for the maximum. After curing at 190°C for 1 h, the exothermic peak on DSC disappeared. All the obtained films of PU/Pa–OMMT were deep yellow and transparent. As the content of OMMT increased, both the tensile modulus and strength of PU/Pa–OMMT films increased, while the elongation decreased. The characteristics of the PU/Pa–OMMT films changed from plastics to elastomers depending on OMMT content and PU/Pa ratio. PU/Pa–OMMT films also exhibited excellent resistance to the solvents such as tetrahydrofuran, N,N‐dimethylformamide and N‐methyl‐2‐pyrrolidinone. The thermal stability of PU/Pa were enhanced remarkably even with small amount of OMMT. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 4075–4083, 2003 |