EIS analysis on low temperature fabrication of TiO2 porous films for dye-sensitized solar cells

A low temperature (<150 °C) fabrication method for preparation of TiO₂ porous films with high efficiency in dye-sensitized solar cells (DSSCs) has been developed. The Ti(IV) tetraisopropoxide (TTIP) was added to the paste of TiO₂ nanoparticles to interconnect the TiO₂ particles. The electrochemical impedance spectroscopy (EIS) technique was employed to quantify the charge transport resistance at the TiO₂/dye/electrolyte interface (R_ct2) and electron lifetime in the TiO₂ film (τ_e) under different molar ratios of TTIP/TiO₂ and also at various TiO₂ thicknesses. It was found that the R_ct2 decreased as the molar ratio increased from 0.02 to 0.08, however, it increased at a molar ratio of 0.2 due to the reduction in surface area for dye adsorption. In addition, the characteristic frequency peak shifted to lower frequency at a molar ratio of 0.08, indicating the longer electron lifetime. As for the thickness effect, TiO₂ film with a thickness around 17 μm achieved the best cell efficiency. EIS study also confirmed that, under illumination, the smallest R_ct2 was associated with a TiO₂ thickness of 17 μm, with the R_ct2 increased as the thickness of TiO₂ film increased. In the Bode plots, the characteristic frequency peaks shifted to higher frequency when the thickness of TiO₂ increased from 17.2 to 48.2 μm, indicating the electron recombination increases as the thickness of the TiO₂ electrode increases.Finally, to make better use of longer wavelength light, 30 wt% of larger TiO₂ particle (300 nm) was mixed with P25 TiO₂ as light scattering particles. It effectively increased the short-circuit current density and cell conversion efficiency from 7.44 to 8.80 mA cm⁻² and 3.75 to 4.20%, respectively.