Defects Analysis on 37CrMnMo4 Drill Pipe Joints |
| |
| WANG Guo-dong,ZHANG Zuo-gui,LIU Jun-liang.Defects Analysis on 37CrMnMo4 Drill Pipe Joints[J].Physics Examination and Testing,2009,27(6):58-58. |
| |
| Authors: | WANG Guo-dong ZHANG Zuo-gui LIU Jun-liang |
| |
| Affiliation: | (Research Institute, Baoshan Iron ＆ Steel Co Ltd,Shanghai 201900,China) |
| |
| Abstract: | Defects in 37CrMnMo4 drill pipe joints are investigated by using optical microscope (OM), scan electron microscope (SEM), energy-dispersive X-ray spectrometry (EDS) and wave-dispersive X-ray spectrometry (WDS). Results show that structure of the drill pipe joints presents over-burnt status, and there are some segregations of P、Mo、Cr around the free crystallization interfaces and in remelted grain boundaries. It is considered that the segregation of Mo、Cr elements should cause deformation burnt in drill pipe joints. |
| |
| Keywords: | drill pipe joints deformation burnt segregation |