Study on TSV isolation liners for a Via Last approach with the use in 3D-WLP for MEMS

This paper discusses approaches for the isolation of deep high aspect ratio through silicon vias (TSV) with respect to a Via Last approach for micro-electro-mechanical systems (MEMS). Selected TSV samples have depths in the range of 170…270 µm and a diameter of 50 µm. The investigations comprise the deposition of different layer stacks by means of subatmospheric and plasma enhanced chemical vapour deposition (PECVD) of tetraethyl orthosilicate; Si(OC₂H₅)₄ (TEOS). Moreover, an etch-back approach and the selective deposition on SiN were also included in the investigations. With respect to the Via Last approach, the contact opening at the TSV bottom by means of a specific spacer-etching method have been addressed within this paper. Step coverage values of up to 74 % were achieved for the best of those approaches. As an alternative to the SiO₂-isolation liners a polymer coating based on the CVD of Parylene F was investigated, which yields even higher step coverage in the range of 80 % at the lower TSV sidewall for a surface film thickness of about 1000 nm. Leakage current measurements were performed and values below 0.1 nA/cm² at 10 kV/cm were determined for the Parylene F films which represents a promising result for the aspired application to Via Last MEMS-TSV.