Tl2Ba2CaCu2O8 thin films on 2 in. LaAlO3(0 0 1) substrates

High quality Tl₂Ba₂CaCu₂O₈ (Tl-2212) superconducting thin films are prepared on both sides of 2 in. LaAlO₃(0 0 1) substrates by off-axis magnetron sputtering and post-annealing process. XRD measurements show that these films possess pure Tl-2212 phase with C-axis perpendicular to the substrate surface. The thickness unhomogeneity of the whole film on the 2 in. wafer is less than 5%. The superconducting transition temperatures T_cs of the films are around 105 K. At zero applied magnetic field, the critical current densities J_cs of the films on both sides of the wafer were measured to be above 2 × 10⁶ A/cm² at 77 K. The microwave surface resistance R_s of film was as low as 350 μΩ at 10 GHz and 77 K. In order to test the suitability of Tl-2212 thin films for passive microwave devices, 3-pole bandpass filters have been fabricated from double-sided Tl-2212 films on LaAlO₃ substrates.