Investigation on one-pot hydrothermal synthesis,structural and optical properties of ZnS quantum dots |
| |
Authors: | N.S. Nirmala Jothi Amish G. Joshi R. Jerald Vijay A. Muthuvinayagam P. Sagayaraj |
| |
Affiliation: | 1. Department of Physics, Loyola College, Chennai 600 034, India;2. CSIR – National Physical Laboratory, Dr. K.S. Krishnan Road, New Delhi 110 012, India;3. Department of Physics, Saveetha School of Engineering, Saveetha University, Chennai 602105, India |
| |
Abstract: | The advantage of hydrothermal synthesis of semiconductor quantum dots (QDs) over the control of particles size, morphology and stability is reported here. In a typical synthesis procedure, the zinc and sulfur precursor molar ratio of 1:3 was used in an aqueous solution at 150 °C. The cubic phase of ZnS with average particles size of 5 nm was confirmed and estimated from the X-ray diffraction (XRD) analysis. The composition and purity of the sample were analyzed from (energy dispersive-ray analysis) EDAX and (X-ray photoelectron spectroscopy analysis) XPS spectra. The absorption spectrum shows the large shift in the absorption band over 90 nm due to the quantum confinement of carriers. The emission spectrum of quantum dots carry more evidence on the presence of shallow trap, deep trap in the band gap of the material responsible for weak emission in the spectral region of 450–500 nm. High resolution transmission electron microscope and scanning electron microscope studies reveal the structural and morphological features of ZnS with slightly distorted spherical morphology. We found that the coordinating ability of solvent strongly influences the reaction process and morphology of the products. |
| |
Keywords: | Chemical synthesis Electron microscopy XPS Optical properties |
本文献已被 ScienceDirect 等数据库收录! |
|