Preparation and Characterization of Nanocrystalline Misch-Metal-Substituted Yttrium Iron Garnet Powder by the Sol–Gel Combustion Process

Nanocrystalline Y_{3? x} MM _x Fe₅O₁₂ powders (MM denotes Misch-metal, x =0.0, 0.25, 0.5, 0.75, and 1.0) were synthesized by a sol–gel combustion method. Magnetic properties and crystalline structures were investigated using X-ray diffraction (XRD), a vibrating sample magnetometer (VSM), and a scanning electron microscope. The XRD patterns showed that the single-phase garnet of Y_{3? x} MM _x Fe₅O₁₂ was formed at x values ≤1.0. The saturation magnetization of powders increased with decreasing MM content and reached the maximum value at Y₃Fe₅O₁₂. The crystallite size of powders calcined at 800°C for 3 h was in the range of 38–53 nm.