| Abstract: | The cationic polymerization of 1,3,5‐trioxane, 1,3‐dioxolane and a small amount of 2‐hydroxyacetic acid (HAA) was carried out, and the resulting modified‐polyacetal (POM) was blended with thermoplastic polyurethane (TPU) in melt. The results of 1H NMR analysis indicated that HAA was almost incorporated in the modified‐POM, and that the resulting carboxyl end‐group and hydroxyl end‐group in the modified‐POM reacted with TPU during the melt blending. There were many boundary layers between the cavities and matrix in the modified‐POM/TPU (82/18 by weight) blend that was etched with tetrahydrofuran (THF), and the diameter of the cavities became ～0.3–1 μm long when the blending time reached 10 min. The results of scanning electron microscopic (SEM) observation and dynamic mechanical analysis (DMA) indicated that the modified‐POM/TPU blend had a good compatibility because of the interfacial reaction between the modified‐POM and TPU phase in the blend. The modified‐POM/TPU blend exhibited higher Charpy impact strength when compared with a normal‐POM/TPU blend; the toughness of the modified‐POM/TPU blend attributed to the good compatibility between the two phases. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 4375–4382, 2006 |