硫冷凝器管接头裂纹原因分析
引用本文:李建宏,杨欣勃,张雪涛,张素英. 硫冷凝器管接头裂纹原因分析[J]. 石油化工设备, 2006, 35(2): 88-90
作者姓名:李建宏  杨欣勃  张雪涛  张素英
作者单位:中国石油,独山子石化分公司,压力容器检验所,新疆,独山子,833600
摘    要:硫磺装置制硫单元硫冷凝器运行较短时间后发生进口侧管接头开裂现象,运行工况和现场检查结果分析认为,冷凝器负荷低与操作工艺不稳定造成壳程液位在管束开裂的部位上下波动,使其产生交变应力并在过程气腐蚀的共同作用下管接头焊缝产生裂纹。对此提出了修复方案和改造措施。

关 键 词:冷凝器  管束  裂纹  角焊缝  腐蚀
文章编号:1000-7466(2006)02-0088-03
修稿时间:2005-10-09

Analysis of the crack at the sulfur condenser bundle corner joint
LI Jian-hong,YANG Xin-bo,ZHANG Xue-tao,ZHANG Su-ying. Analysis of the crack at the sulfur condenser bundle corner joint[J]. Petro-Chemical Equipment, 2006, 35(2): 88-90
Authors:LI Jian-hong  YANG Xin-bo  ZHANG Xue-tao  ZHANG Su-ying
Abstract:Cracking at the corner weld was occurred after short operation for the sulfur making unit of sulfur plant.After the analysis of the working conditions and the site inspecting results,it is concluded that the formation of the cracking at the corner weld was due to low load of the condenser,and shell liquid level fluction at the cracking bundle caused by unstable operating.The repairing methods were presentad.
Keywords:condenser  tube bundle  crack  corner weld  corrosion