| ZG06Cr13Ni4Mo上冠热处理后延时断裂原因分析与控制 |
| |
| 引用本文： | 张忠和. ZG06Cr13Ni4Mo上冠热处理后延时断裂原因分析与控制[J]. 风机技术, 2012, 0(2): 56-57,60 |
| |
| 作者姓名： | 张忠和 |
| |
| 作者单位： | 沈阳鼓风机集团有限公司,辽宁沈阳110869 |
| |
| 摘 要： | 本文就ZG06Cr13Ni4Mo上冠热处理后延时断裂的问题,应用宏观分析、化学分析、金相分析、机械性能检测试验以及断裂失效分析理论,研究其产生的原因,并且改进了工艺,对关键点加强了控制,经几年的实践证明效果很好,再未发生开裂问题。
|
| 关 键 词： | 延时断裂 ZG06Cr13Ni4Mo 工艺试验 |
Reason Analysis and Control of Delay Fracture after ZG06Cr13Ni4Mo Runner Crown Heat Treatment |
| |
| Abstract: | Aiming at the problem of delay fracture after ZG06Cr13Ni4Mo runner crown heat treatment,this paper has analyzed the reasons from the aspects of Macro analysis,chemical analysis,Metallographic analysis,Mechanical properties testing and fracture failure analysis theory.The process is improved and thekeypointsarecontrolled.Itisprovedthat the effect is good by years of practice and withoutfurthercrackingproblem. |
| |
| Keywords: | delay fracture ZG06Cr 13Ni4Mo process test |