| 宋代福建黒釉的施釉工艺 |
| |
| 引用本文： | 刘紫微,张志刚,吴伟,华佳捷,丁敏菊,张成功,李铧. 宋代福建黒釉的施釉工艺[J]. 理化检验(物理分册), 2011, 0(4): 212-216 |
| |
| 作者姓名： | 刘紫微 张志刚 吴伟 华佳捷 丁敏菊 张成功 李铧 |
| |
| 作者单位： | 中国科学院上海硅酸盐研究所高性能陶瓷与超微结构国家重点实验室;上海市公安局物证鉴定中心(上海市现场物证重点实验室——省部共建国家重点实验室培育基地);广西桂林文物商店; |
| |
| 摘 要： | 选取在福建黑釉研究中存在争议的黑釉下出现褐色层的现象开展研究,从显微结构和化学组成两方面对黑釉与褐色层的结构和成分进行比较.结果表明:褐色区域的氧化铁含量明显高于黑釉区域的,而助溶剂含量则低于黑釉区域的,且褐色区域表面存在一层明显的赤铁矿和磁铁矿结晶层;正是这层含铁结晶层的存在导致褐色区域呈现出不同于黑釉的颜色;褐色区...
|
| 关 键 词： | 福建黑釉 施釉工艺 褐色层 显微结构 化学组成 |
Glazing Technology of Fujian Black Glaze of Song Dynasty |
| |
| LIU Zi-wei,ZHANG Zhi-gang,WU Wei,HUA Jia-jie,DING Min-ju,ZHANG Cheng-gong,LI Hua ,shanghai ,.Cultural Store of Guilin Guangxi,Guilin ,China). Glazing Technology of Fujian Black Glaze of Song Dynasty[J]. Physical Testing and Chemical Analysis Part A:Physical Testing, 2011, 0(4): 212-216 |
| |
| Authors: | LIU Zi-wei ZHANG Zhi-gang WU Wei HUA Jia-jie DING Min-ju ZHANG Cheng-gong LI Hua shanghai .Cultural Store of Guilin Guangxi Guilin China) |
| |
| Affiliation: | LIU Zi-wei~1,ZHANG Zhi-gang~1,WU Wei~1,HUA Jia-jie~1,DING Min-ju~2,ZHANG Cheng-gong~2,LI Hua~3 (1.The State Key Lab of High Performance Ceramics and Superfine Microstructure,Shanghai Institute of Ceramics,Chinese Academy of Sciences,Shanghai 200050,China,2.Shanghai Key Laboratory of Crime Scene Evidence,Institute of Forensic Science(State Key Laboratory Breeding Rase of Crime Scene Evidence),shanghai 200083,3.Cultural Store of Guilin Guangxi,Guilin 541000,China) |
| |
| Abstract: | The Fujian black glaze of Song dynasty was investigated due to a controversial phenomenon of brown layer appearing under the black glaze.Microstructure and chemical compositions of the brown layer and the black glaze were characterized by SEM/EPMA.The results show that the content of iron oxide in the brown area was significantly higher than that in the black glaze area,and the solvent content was lower than that in the black glaze area.The surface of brown layer was covered by the hematite and magnetite cr... |
| |
| Keywords: | Fujian black glaze glazing technology brown layer microstructure chemical composition |