Influence of ZrO2 and WO3 doping additives on the thermal properties of porous mullite ceramics

Porous mullite-corundum refractory ceramics were produced by a patented slurry slip casting method from compositions based on commercially available α-Al₂O₃ and γ-Al₂O₃, fused SiO₂ and kaolin. Pores were formed as a result of a chemical reaction of aluminium with water. The influence of usage of raw materials and doping additives such as micro-size ZrO₂ and WO₃ on the sintering temperature, formation of crystalline phases, linear thermal expansion, thermal conductivity and thermal shock resistance of mullite-corundum ceramic was studied. The best thermal shock resistance and, simultaneously, lower thermal conductivity was achieved for the samples doped with WO₃. This was due to the influence of micro-sized WO₃ on the change in γ-Al₂O₃ modification to α-Al₂O₃ and on the structure of mullite ceramics.