Color tunable up-conversion emission of ZrO2:Yb3+, Er3+ thin films prepared by chemical solution deposition

The color-tunable up-conversion (UC) emission was observed in ZrO₂:Yb³⁺, Er³⁺ thin films synthesized on fused silica substrates using a chemical solution deposition method. The crystal structure, surface morphology image and optical transmittance of ZrO₂:Yb³⁺, Er³⁺ thin films were detected in the matter of Yb³⁺/Er³⁺ doping content. Under excitation by 980?nm infrared light, intense UC emission can be obtained from ZrO₂:Yb³⁺, Er³⁺ thin films. Photoluminescence study shows that there are two emission bands centered at 548?nm and 660?nm in the UC luminescence spectra, which can be owing to (²H_11/2,⁴S_3/2)→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 transitions of Er³⁺ ions, respectively. In addition, the color coordinate of UC emission between green-red can be tuned by properly adjusting the dopant concentration, because the composition of Yb³⁺/Er³⁺ affect the red/green ratio via the process of cross relaxation and energy back transfer. Our study suggests that ZrO₂:Yb³⁺, Er³⁺ thin films can be considered as promising materials for new photoluminescence devices.