Mechanical and thermal expansion studies on Ca0.5Sr0.5Zr4-xTixP6O24 ceramics

Ca_0.5Sr_0.5Zr_4-xTi_xP₆O₂₄ (x?=?0?0.2) ceramics belonging to the NZP family were prepared and dense ceramics with no microcracks were obtained. All of the ceramic samples were still composed of the typical NZP structure with a small amount of Ti⁴⁺ substitution for Zr⁴⁺. The mechanical and thermal expansion properties of the ceramics were characterized and the result showed that the flexural strength monotonically increased to 66.5?MPa. The thermal expansion coefficient varied from 1.8 to 3.4?×?10^?6/°C with Ti⁴⁺ content increasing. Thus, it was clear that the substitution of Ti⁴⁺ for Zr⁴⁺ had obvious effects on the sinterability, mechanical and thermal expansion properties of Ca_0.5Sr_0.5Zr_4-xTi_xP₆O₂₄ ceramics, which were discussed in detail.