Color-tunable up-conversion luminescence of Zn(AlxGa1-x)2O4:Yb3+,Tm3+,Er3+ powders

Color-tunable up-conversion powder phosphors Zn(Al_xGa_1-x)₂O₄: Yb³⁺,Tm³⁺,Er³⁺ were synthesized via high temperature solid-state reaction. Also, the morphological and structural characterization, up-conversion luminescent properties were all investigated in this paper. In brief, under the excitation of a 980?nm laser, all powders have same emission peaks containing blue emission at 477?nm (attributed to ¹G₄→³H₆ transition of Tm³⁺ ions), green emission at 526?nm and 549?nm (attributed to ²H_11/2→ ⁴I_15/2 and ⁴S_3/2→⁴I_15/2 transition of Er³⁺ ions respectively), red emission at about 659?nm and 694?nm (attributed to ⁴F_9/2→⁴I_15/2 transition of Er³⁺ ions and ³F₃→³H₆ transition of Tm³⁺ ions, respectively), which are not changed after the doping of Al³⁺ ions. However, the doping of Al³⁺ ions can enhance the up-conversion luminescent intensity and efficiency, while the emission color of as-prepared powder phosphors can be tunable by controlling the doping amount of Al³⁺ ions. Taking Zn(Al_0.5Ga_0.5)₂O₄:Yb,Tm,Er as the cut-off value, the emissions have clear blue-shift firstly and then show obvious red-shift with the increasing doping of Al³⁺ ions. Stated thus, pink emission in ZnAl₂O₄:Yb,Tm,Er, purplish pink emission in ZnGa₂O₄:Yb,Tm,Er and Zn(Al_0.9Ga_0.1)₂O₄:Yb,Tm,Er, purple emission in Zn(Al_0.1Ga_0.9)₂O₄:Yb,Tm,Er and Zn(Al_0.3Ga_0.7)₂O₄:Yb,Tm,Er, purplish blue emission in Zn(Al_0.7Ga_0.3)₂O₄:Yb,Tm,Er, blue emission in Zn(Al_0.5Ga_0.5)₂O₄:Yb,Tm,Er can be observed, which confirm the potential applications of as-prepared Zn(Al_xGa_1-x)₂O₄:Yb³⁺,Tm³⁺,Er³⁺ powder phosphors in luminous paint, infrared detection and so on.