Tribological Properties of DLC Coatings in Helium

The aim of this research work was to investigate tribological properties of low-friction DLC coatings when operating in helium atmosphere. Two commercial DLC coatings (a-C:H and Me-C:H) were included in the investigation and compared to reference PTFE-based coatings, normally used on components operating in helium. Coatings were deposited on hardened 100Cr6 bearing steel discs and tested against uncoated steel balls in low-load pin-on-disc contact configuration. Investigation was focused on the effect of substrate roughness (R _a ?=?0.05?C0.2???m) and contact conditions, including contact pressure (150?C350?MPa) and sliding speed (0.2?C0.4?m/s) on the coefficient of friction of DLC coatings operating in helium. Results of this investigation show that for low-load sliding contact DLC coatings provide low friction in helium atmosphere, similar to soft PTFE-based coatings. At the same time DLC coatings investigated were found to substantially reduce wear of the coated surface. However, while the wear of the coated part has been more or less eliminated, application of DLC coating prolongs running-in and increases wear of the steel counter-part. Furthermore, also in helium atmosphere tribolgical behaviour of DLC coatings showed dependence on the coating type and contact conditions.