Synthesis and functional properties of the Ni1−xMnxFe2O4 ferrites |
| |
Authors: | M AirimioaeiCE Ciomaga N ApostolescuL Leontie AR IordanL Mitoseriu MN Palamaru |
| |
Affiliation: | a Faculty of Chemistry, Al. I. Cuza University, Iasi 700506, Romania b Faculty of Physics, Al. I. Cuza University, Iasi 700506, Romania c Faculty of Chemical Engineering and Environmental Protection, Gheorghe Asachi Technical University of Iasi, 700050, Romania |
| |
Abstract: | Nanocrystalline Ni1−xMnxFe2O4 (x = 0; 0.17; 0.34; 0.5) ferrite powders were successfully synthesized using the sol-gel combustion method, by using nitrates as cations source and citric acid (C6H8O7) as combustion/chelating agent. The reaction advancement was observed by means of IR absorption spectroscopy, by monitoring two characteristic bands for the spinel compounds at about 600 cm−1 and 400 cm−1, respectively. The as-synthesized powders were characterized by IR spectroscopy, X-ray diffraction (XRD) and scanning electronic microscopy (SEM). The magnetic study shows that the saturation magnetization decreases with increasing the Mn addition, as result of the particle size reduction. The dielectric properties were measured as a function of frequency in the range of 10 Hz to 1 MHz. The real part of permittivity has values of ∼88 at 1 kHz and ∼7 at 1 Hz for x = 0. An increasing dielectric permittivity with increasing the amount of Mn is observed. For all the investigated compositions, both the real and imaginary parts of permittivity decrease with frequency. |
| |
Keywords: | Ceramics Sol-gel processes X-ray diffraction Dielectric response Magnetic measurements |
本文献已被 ScienceDirect 等数据库收录! |
|