Reaction-sintering method for ultra-low loss (Mg0.95Co0.05)TiO3 ceramics

Microwave dielectric properties and microstructures of (Mg_0.95Co_0.05)TiO₃ ceramics prepared by a new sintering method (reaction-sintering method) were investigated. A pure phase of (Mg_0.95Co_0.05)TiO₃ was obtained by the new method and excellent dielectric properties were observed due to uniformities of the microstructure and the phase. In contrast, the secondary phase (Mg_0.95Co_0.05)Ti₂O₅ was observed in samples prepared by conventional sintering method. In order to study the influence of secondary phase on the microwave dielectric properties quantitatively, the weight fraction of (Mg_0.95Co_0.05)Ti₂O₅ was calculated on the basis of Rietveld refinement. The pore-free?_r values of specimens prepared by two different methods indicated that porosity plays an important role in the ?_r values of (Mg_0.95Co_0.05)TiO₃ ceramics. Specimens sintered by reaction-sintering method at 1350 °C for 4 h possess excellent dielectric properties with an ?_r of 16.3, a Q × f value of 244,500 GHz, and a τ_f value of −53.5 ppm/°C.