Using the Mass Method to Produce PVC/Clay Nanocomposite Foams: The Effect of Nano-clay and Foaming Conditions on Density and Cell size

Nanocomposite foams contain very fine cells because of the fillers in nano scale. Due to the limited size of the cells, the mechanical and physical properties of nanocomposite foams are improved compared to polymer foams. In this study PVC/clay nanocomposite foams containing various concentrations of nano-clay (1, 3 and 5 phr) were successfully prepared. The samples were placed under CO₂ gas pressure at 5 MPa, by immersing in glycerin bath at 60, 70, 80 °C and 20, 30, 40 s, respectively, to form foams. The density and the cell size as a factor of nano-clay content, foaming time and temperature were investigated using Archimedes method and scanning electron microscopy, respectively. The minimum density was obtained in the sample containing 1 phr nanoclay prepared at 80 °C and 40 s. The minimum cell size was related to the sample containing 5 phr nanoclay at 60 °C and 20 s.