Maskless pendeo-epitaxial growth of GaN films

High-resolution x-ray diffraction (XRD) and atomic force microscopy (AFM) of pendeo-epitaxial (PE) GaN films confirmed transmission electron microscopy (TEM) results regarding the reduction in dislocations in the wings. Wing tilt ≤0.15° was due to tensile stresses in the stripes induced by thermal expansion mismatch between the GaN and the SiC substrate. A strong D°X peak at ≈3.466 eV (full-width half-maximum (FWHM) ≤300 μeV) was measured in the wing material. Films grown at 1020°C exhibited similar vertical 0001] and lateral 11 0] growth rates. Increasing the temperature increased the latter due to the higher thermal stability of the GaN(11 0). The (11 0) surface was atomically smooth under all growth conditions with a root mean square (RMS)=0.17 nm.