High oxide ion conduction in sintered oxides of the system Bi2O3-Y2O3

The ionic conduction in sintered Bi₂O₂-Y₂O₃ was investigated by measuring the conductivity and the emf of an oxygen concentration cell using the specimen tablet as electrolyte. The face centred cubic phase in this system was found to show high oxide ion conduction accompanied by a little electronic conduction when exposed to air. This phase was stable with a composition of 25 ～ 43 mol % Y₂O₃ over a wide range of temperatures, and the oxide ion conductivity increased with decrease in Y₂O₃. The conductivities of (Bi₂O₃)_0.75 (Y₂O₃)_0.25 were 1.6×10^?1 Ω^?1 cm^?1 at 700°C and 1.2×10^?2 Ω^?1 cm^?1 at 500°C values which are many times higher than those of stabilized zirconia (ZrO₂)_0.90(Y₂O₃)_0.10 at corresponding temperatures. Specimens containing less than 25 mol % Y₂O₃ showed a phase transition at 700 ～ 580°C and the conductivities decreased remarkably below these temperatures. High oxide ion conduction in the fcc phase is attributed to the migration of oxide ion vacancies which were present in an appreciable amount.