Li3V2(PO4)3 cathode material synthesized by chemical reduction and lithiation method

The monoclinic-type Li₃V₂(PO₄)₃ cathode material was synthesized via calcining amorphous Li₃V₂(PO₄)₃ obtained by chemical reduction and lithiation of V₂O₅ using oxalic acid as reducer and lithium carbonate as lithium source in alcohol solution. The amorphous Li₃V₂(PO₄)₃ precursor was characterized by using TG–DSC and XPS. The results showed that the V⁵⁺ was reduced to V³⁺ by oxalic acid at ambient temperature and pressure. The prepared Li₃V₂(PO₄)₃ was characterized by XRD and SEM. The results indicated the Li₃V₂(PO₄)₃ powder had good crystallinity and mesoporous morphology with an average diameter of about 30 nm. The pure Li₃V₂(PO₄)₃ exhibits a stable discharge capacity of 130.08 mAh g⁻¹ at 0.1 C (14 mA g⁻¹).