High-rate performance of all-solid-state lithium secondary batteries using Li4Ti5O12 electrode

The all-solid-state Li–In/Li₄Ti₅O₁₂ cell using the 80Li₂S·20P₂S₅ (mol%) solid electrolyte was assembled to investigate rate performances. It was difficult to obtain the stable performance at the charge current density of 3.8 mA cm⁻² in the all-solid-state cell. In order to improve the rate performance, the pulverized Li₄Ti₅O₁₂ particles were applied to the all-solid-state cell, which retained the reversible capacity of about 90 mAh g⁻¹ at 3.8 mA cm⁻². The 70Li₂S·27P₂S₅·3P₂O₅ glass–ceramic, which exhibits the higher lithium ion conductivity than the 80Li₂S·20P₂S₅ solid electrolyte, was also used. The Li–In/70Li₂S·27P₂S₅·3P₂O₅ glass–ceramic/pulverized Li₄Ti₅O₁₂ cell was charged at a current density higher than 3.8 mA cm⁻² and showed the reversible capacity of about 30 mAh g⁻¹ even at 10 mA cm⁻² at room temperature.