Effects of roasting temperature and modification on properties of Li2FeSiO4/C cathode

Li₂FeSiO₄/C cathodes were synthesized by combination of wet-process method and solid-state reaction at high temperature, and effects of roasting temperature and modification on properties of the Li₂FeSiO₄/C cathode were investigated. The XRD patterns of the Li₂FeSiO₄/C samples indicate that all the samples are of good crystallinity, and a little Fe₃O₄ impurity was observed in them. The primary particle size rises as the roasting temperature increases from 600 to 750 °C. The Li₂FeSiO₄/C sample synthesized at 650 °C has good electrochemical performances with an initial discharge capacity of 144.9 mAh g⁻¹ and the discharge capacity remains 136.5 mAh g⁻¹ after 10 cycles. The performance of Li₂FeSiO₄/C cathode is further improved by modification of Ni substitution. The Li₂Fe_0.9Ni_0.1SiO₄/C composite cathode has an initial discharge capacity of 160.1 mAh g⁻¹, and the discharge capacity remains 153.9 mAh g⁻¹ after 10 cycles. The diffusion coefficient of lithium in Li₂FeSiO₄/C is 1.38 × 10⁻¹² cm² s⁻¹ while that in Li₂Fe_0.9Ni_0.1SiO₄/C reaches 3.34 × 10⁻¹² cm² s⁻¹.