Microemulsion preparation and electrochemical characteristics of LiNi1/3Co1/3Mn1/3O2 powders

Layer-structured LiNi_1/3Co_1/3Mn_1/3O₂ was successfully synthesized via a reverse microemulsion (RμE) route. Well-crystallized nanosized (around 45 nm) powders were obtained with calcination at 800 °C. The Rietveld refinement data revealed low degree of cationic displacement in the obtained powders. Within the voltage range of 2.5–4.5 V, the microemulsion-derived LiNi_1/3Co_1/3Mn_1/3O₂ delivered 187.2 and 195.5 mAh g⁻¹ at room temperature and 55 °C, respectively. The prepared powders were found to exhibit low irreversible capacity and good capacity retention. Microemulsion-derived LiNi_1/3Co_1/3Mn_1/3O₂ demonstrated better rate capability than the solid-state derived samples, owing to the reduced particle size and increased surface area. Once the upper cut-off voltage reached 4.6 V, the capacity faded more rapidly than in other operation potential ranges. In this study, the microemulsion process effectively improved the electrochemical characteristics of LiNi_1/3Co_1/3Mn_1/3O₂. This soft chemical route possesses a great potential for synthesizing other types of cathode materials with multiple cations.