B6O–c-BN Composites Prepared by High-Pressure Sintering

High-pressure sintering behavior in the B₆O– c -BN system was investigated using in-laboratory-synthesized B₆O and commercially available c -BN powders (with an average grain size of 0.5, 3, or 6 μm). No reaction occurred between the two components under the high-pressure (4–6 GPa) and high-temperature (1500°–1800°C) conditions that have been investigated. Well-dispersed, sintered B₆O– x ( c -BN) composites (where x = 0–60 vol%) of almost-full density were prepared by sintering at a pressure of 6 GPa and temperature of 1800°C for 20 min. The maximum Vickers microhardness (46 GPa) of these composites was attained by adding 40 vol% c -BN with an average grain size of 0.5 μm. The fracture toughness of these composites increased as the c -BN content increased; the maximum fracture toughness (1.5–1.8 MPa^.m^1/2) was observed for x = 40–60 vol%. Crack deflection along the B₆O– c -BN grain boundary contributed to increasing the fracture toughness.