Fabrication and characterization of 7075 Al alloy reinforced with SiC particulates

7075 aluminum (Al) alloy as matrix and silicon carbide (SiC) as reinforcement has been identified since it has potential applications in aircraft and space industries because of lower weight to strength ratio, high wear resistance and creep resistance. Thorough investigations about the microstructure and characterization of Al alloy/SiC composite are needed so that metal matrix composites (MMCs) fabricated for aircraft and space industries are defect free and have sound microstructure. Objective of this research work are the fabrication and microstructural investigations of AA7075–SiCp MMCs. 7075 Al alloy is reinforced with 10 and 15 wt.% SiCp of size 20–40 μm by stir casting process. The resulting as-cast composite structures are analyzed using scanning electron microscopy, X-ray diffraction (XRD), differential thermal analysis, and electron probe microscopic analysis (EPMA). SiCp distribution and interaction with 7075 Al alloy matrix is studied. The 7075 Al alloy–SiCp composite microstructure showed excellent SiCp distribution into 7075 Al alloy matrix. In addition to this, no evidence of secondary chemical reactions is observed in XRD and EPMA analysis. Decomposition step in derivative thermogravimetric curve is seen at temperature of 1,257, 1,210, and 1,256 °C for 7075 Al alloy, AA7075/10 wt.%/SiCp (20–40 μm) and AA7075/15 wt.%/SiCp (20–40 μm) composites, respectively. So, these composites can be successfully used for applications where temperature does not exceed beyond 1,250 °C.